Journal Article

An <i>ex vivo</i> investigation into the fluoride release and absorption profiles of three orthodontic adhesives

A. K. Coonar, S. P. Jones and G. J. Pearson

in The European Journal of Orthodontics

Published on behalf of European Orthodontics Society

Volume 23, issue 4, pages 417-424
Published in print August 2001 | ISSN: 0141-5387
Published online August 2001 | e-ISSN: 1460-2210 | DOI: http://dx.doi.org/10.1093/ejo/23.4.417
An ex vivo investigation into the fluoride release and absorption profiles of three orthodontic adhesives

More Like This

Show all results sharing this subject:

  • Restorative Dentistry and Orthodontics

GO

Show Summary Details

Preview

Prevention of peri‐bracket decalcification is essentially mediated by effective oral hygiene, which is patient dependent. The potential to compensate for poor oral hygiene may be through the release of free fluoride ions from direct bonding agents. It is well established that glass ionomer cements (GICs) release free fluoride ions which may be replenished by exposure to fluoride containing solutions.

The aim of this ex vivo study was to compare the fluoride release and absorption profiles of a recently developed low fusion, monophase GIC, Limerick glass, with two materials in common clinical use, namely, Fuji‐Ortho L.C. and Concise. Ten test specimens of each material were fabricated and stored in deionized water at 37°C. The concentration of fluoride release was measured daily for the first 7 days after immersion and then weekly for 5 weeks. On day 42 the test specimens were recharged in 2 per cent sodium fluoride solution and fluoride release was measured initially after 24 hours and then every 48 hours. The recharge regimen was repeated for 3 weeks.

Both Limerick glass and Fuji‐Ortho L.C. demonstrated the characteristic fluoride release pattern of GIC with a rapid elution of fluoride after the first 24 hours followed by a more gradual release profile over the following 2 weeks. Fuji‐Ortho L.C. released the greatest quantity of fluoride but the release profile of Limerick glass was more sustained. Concise released negligible amounts of fluoride. Limerick glass and Fuji‐Ortho L.C. showed an increase (P < 0.01) in fluoride release following exposure to 2 per cent sodium fluoride that decreased both with time and subsequent exposures to fluoride supplement.

Journal Article.  0 words. 

Subjects: Restorative Dentistry and Orthodontics

Full text: subscription required

How to subscribe Recommend to my Librarian

Users without a subscription are not able to see the full content. Please, subscribe or login to access all content.