Journal Article

<i>Ex vivo</i> surface and mechanical properties of coated orthodontic archwires

Firas Elayyan, Nick Silikas and David Bearn

in The European Journal of Orthodontics

Published on behalf of European Orthodontics Society

Volume 30, issue 6, pages 661-667
Published in print December 2008 | ISSN: 0141-5387
Published online November 2008 | e-ISSN: 1460-2210 | DOI: http://dx.doi.org/10.1093/ejo/cjn057
Ex vivo surface and mechanical properties of coated orthodontic archwires

More Like This

Show all results sharing this subject:

  • Restorative Dentistry and Orthodontics

GO

Show Summary Details

Preview

This study examined the mechanical and physical properties of retrieved coated nickel–titanium (NiTi) archwires compared with unused samples. Ultraesthetic™ 0.016 inch coated archwires (G&H® Wire Company) were investigated. Ten as-received wires were subjected to a three-point bending test using conventional and self-ligating bracket systems. Surface roughness of the coating was measured with a contact stylus profilometer. Optical and scanning electron microscopes were used to assess surface topography. Ten archwires were used in vivo for a period of between 4 and 6 weeks. Retrieved archwires were subjected to the same tests. The percentage of the remaining coating was calculated using digital photography. Coated archwires were used in vivo for a mean period of 33 days. Differences between the mean values of the as-received and retrieved archwires were determined using t-tests.

In the three-point bending test, with conventional elastomeric ligation, retrieved wires produced a lower unloading force (P < 0.001). Both retrieved and as-received coated archwires produced zero values of unloading force when deflected for 4 mm. When tested using a self-ligating bracket system, retrieved and as-received coated archwires produced the same amount of force (P > 0.05). With surface profilometry, all measured roughness parameters (except Rsm) had greater surface roughness for the retrieved coated archwires (P < 0.05). Under microscopy, retrieved coated archwires showed discolouration, ditching, and delamination. Only 75 per cent of the coating was present in retrieved coated archwires.

Retrieved coated archwires produced lower unloading force values than as-received coated archwires with conventional ligation. Surface roughness of coated archwires increased after use. Coated archwires have a low aesthetic value, with 25 per cent of the coating lost within 33 days in vivo.

Journal Article.  3406 words.  Illustrated.

Subjects: Restorative Dentistry and Orthodontics

Full text: subscription required

How to subscribe Recommend to my Librarian

Users without a subscription are not able to see the full content. Please, subscribe or login to access all content.